IG 2

IG 2

Cementitious Industrial Grout

packagePacking : 25 Kg

IG 2 (Cementitious Industrial Grout) is premixed cementitious, free-flow, non-shrink, high strength, industrial precision grout which is essential to withstand static and dynamic loads. It is a unique product designed to give positive expansion in the plastic and hardened states, producing a low porosity, high durable material. It is carefully designed with fine blended Portland cement, graded sand and other additives for controlled expansion in the plastic state with low water mixing requirement to minimize segregation and deliver high early strength & long-lasting durability.

  • ASTM C 109 / ASTM C 230 / ASTM 109
  • Excellent fluidity and achieve quick strength
  • Can flow through narrow sections
  • Two stage expanding engineering grout
  • Resistant to chemicals, gases etc.
  • Non-flammable, Non corrosive and Non toxic
  • Gaseous expansion system compensates for shrinkage and settlement in the plastic state
  • Easy to remove parts of structure & self-compacting
  • High coverage and economical

  • Suitable for various engineering precision grouting
  • Suitable for grouting of machinery base plates & foundations
  • Grouting of structural column's foundations, masts & fence posts
  • To grout voids, cavities and gaps in concrete
  • Grouting of anchor bolts, various fixings and general purpose grouting in concrete
  • The general purpose grouting of narrow cracks between concrete and metal surfaces

  • Machinery base plates
  • Bearing foundations
  • Turbines & compressors base plates
  • Structural columns & power line stanchions concrete road & structure
  • Pump & other accessories bases
  • Crane tracks, rail posts, dowels and sealing bolts
  • Boiler pumps foundation & anchor
  • bolts Precast structural membrane joints
  • Windows & Doors hole-pars

Testing Parameters Result
Appearence Grey Coloured Powder
Mixing Ratio (25 kg bag) 3.75 - 4.25 lit. of water (15-17%)
Pot Life 15 to 20 minutes
Density of Mixture 2.21 gm/cc
Final Setting Time 4 - 5 hour
Compressive Strength (After 28 days) > 60 Mpa
Flexural Strength (28 days) > 6.5 Mpa
Tensile Adhesion Strength > 2 Mpa
Expansion (%) < 3.5 %

Approx. 10 - 12 sq. ft. / 25 kg bag mix at 12.5 mm bed thickness

Factory sealed packs are best before 12 months from the date of manufacturing in unopened condition and stored in cool & dry area